Obtained ISO9001: 2008 , SGS test GB / T 3880-2006 , EN , ASTM Certified Aluminum Round Bar 6061-T651
Description:
1. Aluminum , Grade: 6061, T6 or T651
2. Hot rolled, Temper & Pre-stretching ,,T651
3.Production leadtime: 25~45days
4. Chemical composition:
Si | Mn | Cr | Zn | Mg | Ti | Fe | Cu |
0.40~0.8 | 0.15max | 0.04~0.35 | 0.25 | 0.8~1.2 | 0.15 | 0.7 | 0.15~0.4 |
5. Tensile strength: σb (MPa):≥180
Yield strength :σ0.2 (MPa):≥110
Elongation rate: δ5 (%):≥14
Machinability
Machinability in the harder T 4 and T6 tempers is good. It is notably less easy to machine in the annealed temper.
Forming
Easily cold worked and formed in the annealed condition. Stamping, bending, spinning, deep drawing are all readily accomplished using standard methods.
Welding
The alloy has very good welding characteristics and may be welded by all of the common welding techniques. Gas tungsten arc welding is generally used for thin sections (less than 0.032") and gas metal arc weld
Obtained ISO9001: 2008 , SGS test GB / T 3880-2006 , EN , ASTM Certified Aluminum Round Bar 6061-T65